Evaluation of a coal seam roof water inrush: case study in the Wangjialing coal mine,China

Mine Water and the Environment - The Wangjialing Mine in southern Shanxi Province is seriously threatened by roof water and is infamous for a water inrush disaster that happened there in 2010. A...     

承钢精粉供应模式探索

承钢探索合理的精粉供应模式,解决了原料场地储存能力小,使用精粉矿点多、成分复杂的不利影响。通过精粉分类、前延管理、系统监控等手段,实现了混合料质量稳定,为烧结系统提供质量稳定的混合料。在目前严峻的市场条件下,探索以管理手段代替占用大量资金的传统料场管理模式的可行性。     

综合物探手段在前道矿山勘查中的应用

介绍了高精度磁法测量和高密度电阻率法测量的原理,并将其应用在前道矿山勘查中。通过对数据解译圈定构造断裂两条,为矿区深部找矿提供了指导。为下一步勘探工作提供了依据。     

胀断连杆用非调质钢C70S6BY产品研发

C70S6BY非调质热轧圆钢经过80 t顶底复吹转炉-LF+VD精炼-240 mm×240 mm方坯连铸-Φ60 mm圆钢连轧-缓冷-精整、探伤工艺生产。采用碱度4~8 Al₂O₃-CaO-SiO₂渣系,LF精炼45~60 min;LF离站［S］≤0.010%,［O］ ≤0.001%;VD后硫合金化,［S］控制在0.063%～0.065%。VD出钢前喂入含镁包芯线100~150 m,Mg收得率在11%~17%,镁硫含量比值约为1.56%。中间包钢水过热度15~30 ℃,铸坯拉速0.9 m/min。经正火后,试验钢抗拉强度和屈服强度达957 MPa和563 MPa;伸长率和断面收缩率达12%和21%。镁改质处理后,硫化物夹杂长宽比1~2占比达到55%以上。     

旋风分离器内气相旋转流不稳定性的实验研究

旋风分离器内气相旋转流具有较强的不稳定性,其表现形式是旋转流的旋转中心围绕几何中心的偏心摆动,导致流场的瞬时速度随时间发生脉动变化。这种旋流的不稳定特性难以用时均流场参数进行描述,需要用动态流场参数描述,为此采用热线风速仪测量了?300 mm旋风分离器内瞬时切向速度随时间的变化。实验结果表明瞬时切向速度是由气体湍流形成的高频脉动和旋转流偏心摆动形成的低频脉动两部分叠加构成,据此探讨了旋转流摆动形成的机制。瞬时切向速度的低频脉动来源于刚性涡的偏心摆动,脉动幅值与偏心距成正比。通过瞬时切向速度频域建立了旋转流的摆动频率与入口速度、筒体直径和排气管直径的计算模型。     

承钢1780线精轧机的减速机螺栓断裂分析

介绍了对承钢1780生产线F1精轧机减速机输入轴固定螺栓和F3精轧机减速机地脚螺栓断裂的断口形貌.对其最大承受力和直径进行了计算,对其微观组织进行了分析,找到了这两起螺栓断裂失效的原因,给出了相应的解决措施.     

融合大数据技术和工艺经验的高炉参数优化

 为了更精准地评判高炉运行情况，量化高炉指导方针。根据高炉生产过程的特点，应用大数据技术对高炉生产参数与铁水产量和高炉能耗等指标进行数据驱动分析，提出了一种优化高炉生产参数的新方法。首先，对某钢铁厂高炉各工序历史数据进行了采集、清洗、过滤和整合，建立了高炉数据仓库。然后，将多种聚类算法相结合，完成了对高炉炉况变化的详细划分。运用工艺经验与递归特征消除算法相结合，全面筛选得到能够反映炉况波动的强相关变量。应用统计学方法分析得出Class_a炉况对应的核心参数的最优范围，这对指导现场生产、保持高炉长期稳定顺行具有重要意义。     

半钢炼钢转炉干法除尘系统泄爆分析及应对措施

对承钢120 t半钢炼钢转炉干法除尘泄爆进行调查、统计和分析。分析了泄爆发生的主要原因,并提出了相应的改进措施。通过优化开吹供氧曲线和规范冶炼操作,泄爆次数逐月减少,稳定了转炉的生产节奏,提高转炉的产能,减少除尘设备的损害。     

Low shear rheological behaviour of two-phase mesophase pitch

The low shear rate rheology of two phase mesophase pitches derived from coal tar pitch has been investigated. Particulate quinoline insolubles (QI) stabilised the mesophase spheres against coalescence. Viscosity measurements over the range 10–10⁶ Pa s were made at appropriate temperature ranges. Increasing shear thinning behaviour was evident with increasing mesophase content. At low mesophase contents the dominant effect on the near Newtonian viscosity was temperature but at higher contents it was the shear rate; temperature dependence declined to near zero. The data indicated that agglomeration could be occurring at intermediate mesophase volume fractions, 0.2–0.3. The Krieger–Dougherty function and its emulsion analogue indicated that in this region the mesophase pitch emulsions actually behaved like ‘hard’ sphere systems and the effective volume fraction was estimated as a function of shear rate illustrating the change in extent of agglomeration. At the higher volume fractions approaching the maximum packing fraction, which could only be measured at higher temperatures, the shear thinning behaviour changed in character and it is considered that this is possibly due to shear induced deformation and breakup of dispersed drops in the shear field.     

新型提渣装置在步进式加热炉上的开发应用

针对步进式加热炉炉底出渣较困难的情况,分析氧化铁皮渣产生的原因,开发了一种新型提渣装置,以解决炉底地坑内堆积炉渣的清理问题,实现了无需用天车即可将炉底氧化铁皮渣运至地面以上。通过以上工作,承钢成功研制了一种步进式加热炉炉底提渣专利装置。